Nafion® and Polyaniline Composite Modification with Li and Mg Ions

Functional Materials and Nanotechnologies (FM&NT 2018). IOP Conference Series: Materials Science and Engineering. Vol.503 2019
Staņislavs Ložkins, Jūlija Hodakovska, Jānis Kleperis, Remo Merijs-Meri

Modification of Nafion®-based samples with polyaniline (PANI) and positive charged ions could potentially allow achieving good proton conductivity at higher working temperatures what is observed in typical polymer electrolyte membrane fuel cells. In this work Nafion® polymer was modified with 1% polyaniline emeraldine salt and Li and Mg ions containing solutions. The influence of activation process and the type of ions on composites' proton conductivity was investigated. To define the best composition the physiochemical properties of synthesized materials were determined by the means of thermogravimetric analysis, impedance spectroscopy, determination of water absorption and its kinetics, and FTIR. From the original samples the best results of σ=155 mS/cm were shown by Nafion®/PANI membrane what was modified by Li+ reduction solution. This membrane also had better thermal characteristic compared to other researched samples: membrane degradation starts on higher temperature interval.

Keywords
leucoemeraldine; emeraldine; membranes
DOI
10.1088/1757-899X/503/1/012031
Hyperlink
https://iopscience.iop.org/article/10.1088/1757-899X/503/1/012031

Ložkins, S., Hodakovska, J., Kleperis, J., Merijs-Meri, R. Nafion® and Polyaniline Composite Modification with Li and Mg Ions. In: Functional Materials and Nanotechnologies (FM&NT 2018). IOP Conference Series: Materials Science and Engineering. Vol.503, Latvia, Riga, 2-5 October, 2018. Bristol: IOP Publishing, 2019, Article number 012031. ISSN 1757-8981. e-ISSN 1757-899X. Available from: doi:10.1088/1757-899X/503/1/012031