Structure, Micromechanical and Magnetic Properties of Polycarbonate Nanocomposites
IOP Conference Series: Materials Science and Engineering 2013
J. Maniks, R. Zabels, Remo Merijs-Meri, Jānis Zicāns

The current study evaluates the applicability of polycarbonate (PC) for development of magnetic polymer nanocomposites with CoFe2O4 nanofiller, the amount of which was changed from 0 to 5 wt. %. Ethylene-vinyl acetate elastomer in the amount of 10 wt. % was added as toughener. Upon introduction of the magnetic filler a magnetic hysteresis loop was observed: at 5 wt.% of CoFe2O4 saturation magnetization of the nanocomposite was 2,2 emu/g, remanent magnetization was 0,8 emu/g and coercivity is 1200 G. Nanoindentation tests showed that nanofiller-reinforced samples maintain reasonable plasticity characterized by work of plastic indentation, while their modulus and hardness were improved by up to 14% and 20%, correspondingly. Structural study revealed clustering of the nanofiller at the contents above 2 wt.% that led to reduction of strengthening effect.


Atslēgas vārdi
Polycarbonate Nanocomposites ,Structure, Micromechanical Properties , Magnetic Properties
DOI
10.1088/1757-899X/49/1/012012
Hipersaite
http://iopscience.iop.org/1757-899X/49/1/012012/

Maniks, J., Zabels, R., Merijs-Meri, R., Zicāns, J. Structure, Micromechanical and Magnetic Properties of Polycarbonate Nanocomposites. IOP Conference Series: Materials Science and Engineering, 2013, Vol.49, Iss.1, 012012.-012012.lpp. ISSN 1757-8981. e-ISSN 1757-899X. Pieejams: doi:10.1088/1757-899X/49/1/012012

Publikācijas valoda
English (en)
RTU Zinātniskā bibliotēka.
E-pasts: uzzinas@rtu.lv; Tālr: +371 28399196