Publikācija: Influence of Fillers on the Alkali Activated Chamotte

Publikācijas veids Publikācijas konferenču materiālos, kas ir indeksēti Web of Science un/vai SCOPUS
Pamatdarbībai piesaistītais finansējums Citi pētniecības projekti
Aizstāvēšana: ,
Publikācijas valoda English (en)
Nosaukums oriģinālvalodā Influence of Fillers on the Alkali Activated Chamotte
Pētniecības nozare 2. Inženierzinātnes un tehnoloģijas
Pētniecības apakšnozare 2.1. Būvniecības un transporta inženierzinātnes
Pētniecības platforma Neviena
Autori Laura Dembovska
Ģirts Būmanis
Laura Vītola
Diāna Bajāre
Atslēgas vārdi chamotte
Anotācija Alkali-activated materials (AAM) exhibit remarkable high-temperature resistance which makes them perspective materials for high-temperature applications, for instance as fire protecting and insulating materials in industrial furnaces. Series of experiments were carried out to develop optimum mix proportions of AAM based on chamotte with quartz sand (Q), olivine sand (OL) and firebrick sawing residues (K26) as fillers. Aluminium scrap recycling waste was considered as a pore forming agent and 6M NaOH alkali activation solution has been used. Lightweight porous AAM have been obtained with density in range from 600 to 880 kg/m3 and compressive strength from 0.8 to 2.7 MPa. The XRD and high temperature optical microscopy was used to characterize the performance of AAM. The mechanical, physical and structural properties of the AAM were determined after the exposure to elevated temperatures at 800 and 1000°C. The results indicate that most promising results for AAM were with K26 filler where strength increase was observed while Q and OL filler reduced mechanical properties due to structure deterioration caused by expansive nature of selected filler.
DOI: 10.1088/1757-899X/251/1/012009
Hipersaite: http://iopscience.iop.org/journal/1757-899X 
Atsauce Dembovska, L., Būmanis, Ģ., Vītola, L., Bajāre, D. Influence of Fillers on the Alkali Activated Chamotte. No: IOP Conference Series: Materials Science and Engineering, Latvija, Riga, 27.-29. septembris, 2017. Riga: IOP Publishing, 2017, 1.-8.lpp. ISSN 1757-8981. e-ISSN 1757-899X. Pieejams: doi:10.1088/1757-899X/251/1/012009
Papildinformācija Citējamību skaits:
ID 26552