Publikācija: Compressive Failure of Quasi-Static Indented CFRP / Aluminium Honeycomb Sandwich Panels

Publikācijas veids Publikācijas konferenču materiālos, kas ir indeksēti Web of Science un/vai SCOPUS
Pamatdarbībai piesaistītais finansējums Pētniecības projekti
Aizstāvēšana: ,
Publikācijas valoda English (en)
Nosaukums oriģinālvalodā Compressive Failure of Quasi-Static Indented CFRP / Aluminium Honeycomb Sandwich Panels
Pētniecības nozare 2. Inženierzinātnes un tehnoloģijas
Pētniecības apakšnozare 2.1. Būvniecības un transporta inženierzinātnes
Pētniecības platforma Materiāli, procesi un tehnoloģijas
Autori Guntis Japiņš
Kaspars Kalniņš
Olģerts Ozoliņš
Eduards Skuķis
Atslēgas vārdi quasi-static; honeycomb; sandwich panels; carbon fiber; damage
Anotācija The present study examines sandwich panels, which are made of carbon fiber facesheets with aluminium honeycomb core and focuses on how varying factors (skin thickness, layup, core density and diameter of hemispherical indenter) are affecting collapse of artificially damaged panels in edgewise compression. Damage in the middle of sandwich specimens was introduced using quasi-static indentation. Hemispherical indenters of two diameters, namely, 20 mm and 150 mm, were applied. The residual strength was estimated through the edgewise compression test of damaged specimens. The study demonstrated that increase of the honeycomb density led to decrease in the safety margin in structure. Thicker skins may also lead to a catastrophic propagation of indent.
DOI: 10.1088/1757-899X/500/1/012007
Hipersaite: https://iopscience.iop.org/article/10.1088/1757-899X/500/1/012007 
Atsauce Japiņš, G., Kalniņš, K., Ozoliņš, O., Skuķis, E. Compressive Failure of Quasi-Static Indented CFRP / Aluminium Honeycomb Sandwich Panels. No: IOP Conference Series: Materials Science and Engineering, Latvija, Jurmala, 12.-14. septembris, 2018. IOP PUBLISHING LTD, DIRAC HOUSE, TEMPLE BACK, BRISTOL BS1 6BE, ENGLAND: IOP Publishing, 2019, 1.-7.lpp. ISSN 1757-8981. e-ISSN 1757-899X. Pieejams: doi:10.1088/1757-899X/500/1/012007